Stainless steel grades for corrosive environments
Hot alkaline environment
In the alkaline environment of pulp mills, uniform corrosion is the typical corrosion mechanism. Laboratory tests and industry experience have shown that lean duplex grades Forta
EDX 2304 perform well in these conditions. Surprisingly the “acid proof” molybdenum alloyed stainless steel grades like 316L suffer from rapid deterioration. In addition, duplex grades show superior stress corrosion cracking resistance in alkaline environment compared to 304L.
Acidic chlorine environment
In an acidic chlorine environment, the key to enhancing the corrosion resistance of stainless steel is the introduction of increased chromium, molybdenum and nitrogen content. With that in mind, austenitic high-alloyed grades like Ultra
254 SMO and Ultra
904L are well suited to the conditions, with duplex grades Forta
SDX 2507 and Forta
DX 2205 also exhibiting similar corrosion resistance combined with high mechanical strength and leaner alloying of volatile elements. In all cases, performance can be assessed with the help of PREN (Pitting Resistance Equivalent) and CPT (Critical Pitting Temperature) values.
Hot water and chlorides
Typical austenitic stainless steels such as 304L and 316L are susceptible to stress corrosion cracking due to warm, chloride-heavy environments – generally at temperatures above 50°C. High-alloyed austenitic Ultra
grades however show much better performance and Duplex stainless steels
, thanks to their austenitic-ferritic microstructure, are extremely resistant in these conditions. The stainless steel grade selection depends on the conditions and can vary from the leanest – Forta
LDX 2101, right up to Forta
Weight savings and cost predictability with duplex solution
Compared to austenitic grades, duplex stainless steels are generally lean with volatile and expensive alloying elements such as nickel and molybdenum. Forta
LDX 2101 lean duplex is an extreme example of this: It's corrosion resistance is achieved mainly by the alloying of chromium and nitrogen, while it's nickel content is only 1.5%. Duplex grades have high mechanical strength, which enables considerable weight savings in pulp & paper industry applications – such as pressure vessels and various types of processing and storage tanks. As such, duplex grades make for optimal construction materials for capital investment projects that require cost predictability.
Figure: Lean duplex provides superior price predictability over 304L and 316L due to its lean alloying concept.